High chlorinated polyethylene finish

Basic parameters

Also known as high chlorinated finish, HCPE finish

Color Grey

Ratio of one or two components: Main agent: curing agent =20:5

Construction brush coating, spraying, rolling coating can be

The composition is composed of high chlorinated polyethylene resin, anti-rust pigment, filler, auxiliary agent, solvent and so on.

Product characteristics

• Excellent anti-corrosion properties. High chlorinated polyethylene coating has excellent anti-corrosion properties, and can resist the penetration of moisture, oxygen, ions (such as Cl-, SO42-). The permeability of its paint film is very low, about 1/200 to 1/300 of alkyd resin, and 1/2 of pervinyl chloride and chlorosulfonated polyethylene, which makes it still able to maintain good anti-corrosion effect in harsh environment2.
• Good weather resistance. Because high chlorinated polyethylene resin does not contain double bonds, it is not sensitive to photochemical reaction and oxidative degradation, so the paint film can remain stable under the action of outdoor atmosphere, ultraviolet light, oxygen and cold and heat changes, and has good weather resistance.
• Excellent mechanical and physical properties. High chlorinated polyethylene paint film has excellent mechanical and physical properties. In addition, it also has water resistance, acid and alkali resistance, chemical resistance and other properties.
• Technical requirements

Product use

Not only suitable for indoor and outdoor all kinds of metal and concrete rust protection, but also especially suitable for railway Bridges, high voltage transmission towers, containers, offshore oil equipment, storage tanks, Bridges and large steel structure equipment protection.

Construction parameters

Construction structure drawing:

Supporting scheme:

• Epoxy zinc-rich primer/epoxy primer/inorganic zinc-rich primer/graphene zinc powder primer, etc. + epoxy cloud iron intermediate paint/epoxy thick paste intermediate paint/high chlorinated polyethylene primer + high chlorinated polyethylene intermediate paint/epoxy cloud iron intermediate paint/epoxy thick paste intermediate paint + high chlorinated polyethylene top paint

Construction precautions:

• The temperature of the substrate must be above the dew point of 3℃, when the temperature of the substrate is below 5℃, the paint film is not solidified, and it is not suitable for construction.
• In the high temperature season construction, easy to occur dry spray, in order to avoid dry spray can be adjusted to dry spray until the diluent.
• This product should be used by professional painting operators according to the product packaging or the instructions in this manual.

Steel surface:

• Must thoroughly remove oil, rust, etc., to achieve the rust removal standard Sa2.5, the roughness of 30um-75um; Adopt manual rust removal method, need to reach the rust removal standard St3 level.

Concrete surface:

The surface of the concrete should be flat, dry, no seepage floating water and water. The base that has been polluted by grease and chemicals can be washed with detergent, lye or solvent, and can also be treated by fire baking, steam blowing, etc., but it must not damage the base.

Precautions

Products should be stored in a cool and ventilated place to prevent rain, direct sunlight, avoid collision, need to isolate the fire source.

The construction site is strictly prohibited fireworks, painters should wear glasses, gloves, masks, etc., to avoid skin contact and inhalation of paint mist.

All work on the coating and use of this product must be done in accordance with various relevant national health, safety and environmental regulations and standards.

If you have any questions about the use of this product, please contact our technical service department.